Method for the production of an elastic laminate and laminated elastic product

ABSTRACT

A method for the production of an elastic laminate, with the following steps in a production line: coextrudeing a first web of elastic film with at least three layers, with at least two different polymer materials, to feed contemporaneously said coextruded first elastic film web and two second nonwoven webs to a thermal, binding calender, wherein the first elastic film web is arranged between said two second nonwoven webs when entering the calender; wherein said first elastic film web, during the movement from the coextrusion step to the thermal binding step, passes from a melted state, to a solidified and cold state when entering the calender, to join, through spot welding in said calender, said second nonwoven webs with respective opposite outer layers of said first elastic film web, thus producing an intermediate web, to stretch mechanically said intermediate web according to a direction transverse to the same web.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional under 37 CFR 1.53(b) of pending prior U.S. patent application Ser. No. 15/756,461 filed Feb. 28, 2018, which claims the benefit (35 U.S.C. § 120 and 365(c)) of International Application PCT/IB2016/055167 filed Aug. 30, 2016, and claims the benefit of priority under 35 U.S.C. § 119 of Italian Application UB2015A003333, filed Sep. 1, 2015, the entire contents of each application are incorporated herein by reference.

FIELD OF THE INVENTION

The present invention relates to flexible elastic sheets or, more generally, laminates, comprising elastic films joined with nonwovens, to be used, for example, in hygienic and sanitary products, etc., like closures or parts of diapers, panty liners, and other products.

More in particular, the object of the invention is a method for the production of an elastic laminate and a laminated elastic product produced by means of said method.

BACKGROUND OF THE INVENTION

As it is well known, hygienic and sanitary products, such as diapers, bandages, paper napkins, disposable clothes etc. have required, for a long time, high technical and “sensorial” performances. This kind of products often requires optimal elastic features, for instance in order to be used to realize closures or other portions of baby diapers. These products shall be not only able to elongate, but also provided with adequate tensile strength, even after a certain number of cycles. Another important aspect is that these products shall be pleasant to the touch, for instance soft, in correspondence of the interface between product and user contact area. At the same time, they shall ensure adequate strength during use and a particularly light and non “invasive” look. The products currently available on the market are not able to satisfy all these requirement at the same time; above all, they are not able to ensure adequate softness, elasticity and strength at the same time.

SUMMARY OF THE INVENTION

The main object of the present invention is to provide a production method allowing to produce an elastic laminate, especially, but without limitation, for hygienic and sanitary products etc., having high elasticity, high tensile strength and increased softness with respect to the known products.

This and other objects, which will be better explained below, are achieved by means of a method for the production of an elastic laminate, comprising the following steps in a same production line:

-   -   to coextrude a first web of elastic film with at least three         layers, comprising at least two different polymer materials,     -   to feed contemporaneously said coextruded first elastic film web         and two second nonwoven webs to a thermal binding calender,         wherein the first elastic film web is arranged between said two         second nonwoven webs when entering the calender; wherein said         first elastic film web, during the movement from the coextrusion         step to the thermal binding step, passes from a melted state, in         the coextrusion step, to a solidified and cold state when         entering the calender,     -   to join, through spot welding in said calender, said second         nonwoven webs with respective opposite outer layers of said         first elastic film web, thus producing an intermediate web,     -   to stretch mechanically said intermediate web according to a         direction transverse to the same web.

The production line provides for the continuous feeding of the three webs, from a starting area up to a collection area downstream of the stretching area. As well known, the web feeding direction, or at least the feeding direction of the intermediate web after the calender, is called MD-Machine direction, whilst the direction transverse to MD is called CD-Cross Direction. Therefore, the webs are preferably fed continuously along the line, or at least through the calender. Once the intermediate web has been stretched, it can be cut into portions of the desired length, that can be wound and stored.

Welding spots or areas means regions or areas of discrete dimensions, formed due to the effect of heat and pressure exerted by protuberances provided on a calender roller. Shape and dimensions of the welding spots or areas are similar or derive from the shape and dimensions of the protuberance vertexes. They may be, for instance, round or oval, or may have irregular shape, like “islands”, Le. welding areas surrounded by non-welding areas. The regions or areas may have equal shape and/or dimensions, or they may have different shape and/or dimensions, or they may have partially equal shape and/or dimensions.

The calender is preferably equipped with two rollers: one is a flat contrast roller, the other is provided with protuberances forming the discrete welding spots or areas.

For the mechanical stretching step in CD a station is for example provided, comprising two cylinders, which are arranged above each other, between which the web passes and which are provided with rings equally spaced from one another; the rings of one cylinder enter the spaces between the rings of the other cylinder, thus transversally stretching the intermediate web that has been laminated in the calender.

The coextruded elastic film has preferably a temperature, when entering the calender, equal to, or lower than, 1/7 of the temperature the elastic film has at the end of the coextrusion step; this temperature is preferably lower than 1/10; at the end of the coextrusion step, the elastic film has a temperature preferably comprised between 220° C. and 270° C., while, when entering the calender, said coextruded elastic film has a temperature preferably comprised between 10° C. and 40° C., and more preferably between 15° C. and 35° C.

Preferably, after the extrusion step and before the joining step, i.e. before entering the calender, the film passes through a cooling station, for example a pair of cooling rollers, in order to achieve a temperature similar to the temperature it has when entering the calender, i.e. a temperature comprised between 10° C. and 40° C., and more preferably between 15° C. and 35° C.

The cooling contributes to structure the elastic film adequately, so that, thanks to the lamination in the calender and the subsequent stretching step, the final laminate is particularly elastic, resistant and soft.

In order to facilitate the cooling, the first web of coextruded elastic film may adequately travel, from the extrusion step to the entrance into the calender, an air path comprised between 5 m, and 20 m, and more preferably comprised between 8 m and 13 m, at ambient temperature.

Preferably, before the stretching step and after the heat-welding step the intermediate web may be cooled up to a temperature comprised between 15° C. and 40° C., for example by means of a pair of known cooling rollers.

Preferably, the elastic film comprises exactly three layers, wherein the ratio between the sum of the thicknesses of the two outer layers and the thickness of the inner layer of the coextruded elastic film entering the calender is comprised between ⅓ and 1/25 and more preferably between 1/7 and 1/21.

The thickness of the elastic film is preferably comprised between 0.04 mm and 0.14 mm. These ratios allows to achieve, for example, optimal performance in terms of elasticity and strength, ensuring at the same time the required softness of the final laminate. Adequately, the two outer layers of the elastic film may be made of the same polymer material and preferably have the same thickness.

One or more layers of the elastic film are preferably made of one or more of the following materials: elastomers: poly (ethylene-butene), poly (ethylenehexene), poly (ethylene-octene), poly (ethylene-propylene), poly (styrenebutadiene-styrene), poly (styrene-isoprene-styrene), poly (styrene-ethylenebutylene-styrene), poly (ester-ether), poly (ether-amide), poly (ethylene-vinyl acetate), poly (ethylene-methyl acrylate), poly (ethylene-acrylic acid), poly (ethylene butyl acrylate), polyurethane, poly (ethylene-propylene-diene), ethylene-propylene rubber.

One or more layers of the elastic film may be also made of polymers similar to rubber, for example polymers made of polyolefins produced by singlesite catalysts.

One or more layers of the elastic film may be also made of polymers produced by means of known catalysts, for example metallocene catalysts; for example, ethylene, propylene and other olefins may be polymerized with butene, hexene, octene etc. in order to obtain elastomers like poly (ethylenebutene), poly (ethylene-hexene), poly (ethylene-octene), poly (ethylene-propylene) and/or polyolefin terpolymers thereof, suitable for one or more layers of the elastic film.

One or more layers of the elastic film may be made of polyolefin elastomers, such as Dow®Infuse™, ExxonMobile®, Vistamaxx®, and the like; and/or a combination thereof or other adequate elastic material.

According to preferred embodiments, the second nonwoven webs have substantially equal dimensions and composition. In the present description, the term “fibers” generically means both fibers, short or long, and filaments. Preferably, at least one of the second nonwoven webs (and preferably both the webs) is a spun bound web. Moreover, one or more second webs may be carded, heat-sealable and extendible.

According to preferred embodiments, at least part of the materials forming the outer layers of the elastic film are thermally compatible with at least part of the materials forming the fibers of the nonwoven web they respectively face. Thermal compatibility means the ability of two materials to remain joined together after heat-welding, or to remain joined together when they are thermally fused above each other and then cooled. For example, FIG. 3 shows a table with a matrix, wherein in the columns and in the rows some materials are indicated, and X indicates that the material in the row and the material in the column are thermally compatible.

Preferably, at least one nonwoven web (and preferably both the w˜bs) has a thickness, before entering the calender, comprised between 0.1 mm and 0.6 mm, and more preferably between 0.15 mm and 0.5 mm. In this description, the thickness has been measured according to EDANAWSP 120.6.

Preferably, at least one nonwoven web (and preferably both the webs) has a weight, before entering the calender, comprised between 10 and 40 g/m², measured according to EDANA WSP 130.1. The nonwovens are preferably extendible and non-elastic. This means that, when subjected to traction, they can elongate, but do not have an elastic behavior.

According to preferred embodiments, the temperature of the calender rollers is comprised between 120° C. and 160° C. Preferably, the lamination pressure between the calender rollers is comprised between 50 kg/cm² and 200 kg/cm². The final thickness of the laminated product P at the end of processing is preferably comprised between 0.4 mm and 2 mm, and more preferably between 0.5 mm and 1.5 mm. The weight of the laminated product P, at the end of processing, is preferably comprised between 50 and 140 g/m².

According to preferred embodiments, the thickness of the laminated product exiting the production line has an increased thickness with respect to the sum of the single nonwoven webs and the elastic film entering the calender, and this increment is comprised between 50% and 66%.

According to preferred embodiments:

-   -   the ratio between MD elongation at break at 10 N and laminate         thickness after the stretching step is lower than 8, and         preferably lower than 7.5, 15 and/or     -   the ratio in (N/50 mm)/(mm), between CD tensile strength and         laminate thickness after the stretching step is lower than 79,         and preferably lower than 78, and/or     -   the ratio in (g/m 2/mm) between laminate weight and thickness         after the 20 stretching step is lower than 105, and more         preferably lower than 100.

The MD elongation has been measured according to EDANA WSP 110.4; the tensile strength has been measured according to EDANA WSP 110.4, with the only exception of the specimen, that, instead of having a dimension of 50×80 mm, was an isosceles trapezoid with the smaller base equal to 55 mm, 25 the longer base equal to 95 mm and the height equal to 80 mm; the grammage has been measured according to EDANA WSP 130.1; the thickness has been measured according to EDANA WSP 120.6.

According to preferred embodiments, the welding spot or welding area density is comprised between 15 and 60 spots/cm². Preferably, the welding spots or areas are distributed on the whole area of the laminated product homogeneously and/or uniformly.

A further object of the present invention is an elastic laminate, to be especially used, but without limitation, for hygienic and sanitary products etc., for instance closures for diapers, having high elasticity, high tensile strength and increased softness with respect to known products; the elastic laminate comprises:

-   -   a polymer intermediate elastic film formed by three coextruded         layers, wherein the outer layers are made of the same polymer         material, and the inner layer is made of a different polymer         material,     -   two nonwoven fabrics joined, through spot or area welding, to         respective outer layers of the coextruded elastic film;         and wherein     -   the ratio between MD elongation at break at 10 N and laminate         thickness after the stretching step is lower than 8, and         preferably lower than 7.5, and/or     -   the ratio in (N/50 mm)/(mm), between CD tensile strength and         laminate thickness after the stretching step is lower than 79,         and preferably lower than 78, and/or     -   the ratio in (g/m²/mm) between laminate weight and thickness         after the stretching step is lower than 105, and more preferably         lower than 100.

As above, the MD elongation has been measured according to EDANA WSP 110.4; the tensile strength has been measured according to EDANA WSP 110.4, with the only exception of the specimen, that, instead of having a dimension of 50×80 mm, was an isosceles trapezoid with the smaller base equal to 55 mm, the longer base equal to 95 mm and the height equal to 80 mm; the grammage has been measured according to EDANA WSP 130.1; the thickness has been measured according to EDANA WSP 120.6.

Preferably, the welding spot or welding area density is comprised between 15 and 60 spots/cm². The thickness of the laminated product P is preferably comprised between 0.5 mm and 1.5 mm. The weight of the laminated product P, at the end of processing, IS preferably comprised between 60 and 140 g/m².

One or more layers of the elastic film are preferably made of one or more of the following materials: elastomers: poly (ethylene-butene), poly (ethylenehexene), poly (ethylene-octene), poly (ethylene-propylene), poly (styrenebutadiene-styrene), poly (styrene-isoprene-styrene), poly (styrene-ethylenebutylene-styrene), poly (ester-ether), poly (ether-amide), poly (ethylene-vinyl acetate), poly (ethylene-methyl acrylate), poly (ethylene-acrylic acid), poly (ethylene butyl acrylate), polyurethane, poly (ethylene-propylene-diene), ethylene-propylene rubber.

One or more layers of the elastic film may be also made of polymers similar to rubber, for example polymers made of polyolefins produced by single-site catalysts.

One or more layers of the elastic film may be also made of polymers produced by means of known catalysts, for example metallocene catalysts; for example, ethylene, propylene and other olefins may be polymerized with butene, hexene, octene etc. in order to obtain elastomers like poly (ethylene-butene), poly (ethylene-hexene), poly (ethylene-octene), poly (ethylenepropylene) and/or polyolefin terpolymers thereof, suitable for one or more layers of the elastic film.

One or more layers of the elastic film may be made of polyolefin elastomers, such as Dow®Infuse™, ExxonMobile®, Vistamaxx®, and the like; and/or a combination thereof or other adequate elastic material. Preferably, the second nonwoven webs have substantially equal dimensions and composition. Preferably, at least one of the second nonwoven webs (and preferably both the nonwoven webs) has bicomponent fibers, preferably of the coaxial type. The bicomponent fibers preferably comprise PP and PE. Preferably, at least one of the second nonwoven webs (and preferably both the webs) is a spun bound web. One or more of the second webs may be made of monofilament fiber, for example polypropylene, and may be a spun bound web. Moreover, one or more of the second webs may be carded, heat-sealable and extendible.

According to preferred embodiments, at least part of the materials forming the outer layers of the elastic film are thermally compatible with at least part of the materials forming the fibers of the nonwoven web with which it is into contact.

BRIEF DESCRIPTION OF THE DRAWINGS

In the drawings:

FIG. 1 is a scheme of a plant for implementing the method according to the invention;

FIG. 2 is a schematic cross section of a laminated product according to the invention;

FIG. 3 is a table showing the thermal compatibility of materials.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

With reference to the previously mentioned figures, number 10 indicates, as a whole, a plant for implementing a production method allowing to produce an elastic laminate especially, but without limitation, suitable for hygienic and sanitary products etc., having high elasticity, high tensile strength and increased softness with respect to known products.

This plant comprises an extruder 11 suitable to coextrude a multi-layer elastic film made of polymer material F.

In this example, the extruder 11 allows the coextrusion of a three-layer film, with the outer layers F1 having the same thickness and being made for example with polyolefin elastomers, for instance Dow®Infuse™, ExxonMobile® Vistamaxx®, and the like, together with polyolefin polymers like poly (ethylenebutene), poly (ethylene-hexene), poly (ethylene-octene), poly (ethylenepropylene) and or polyolefin thermoplastic polymers thereof. The inner layer F2 is made, for example, of one or more of the following materials: block copolymers containing SBS (styrene-butadiene-styrene), SIS (styrene-isoprene-30 styrene, SEBS (styrene-ethylene-butylene-styrene) and polyolefin elastomers like Dow®Infuse™, ExxonMobile® Vistamaxx®, and the like.

In this example, the inner layer is a combination of SEBS (styrene-ethylene-butylene-styrene) and the outer layers are based on one or more polyethylene polymers.

The film is substantially impermeable and not transpiring. The extruder may have a roller, not shown in the figures, for depositing the film as it exited the extruder mouth.

Downstream of the extruder 11, a cooling station R of the known type is provided, formed, for example, by two cooled rollers, between which the film from the extruder is fed.

The plant also comprises two areas 12 and 13, occupied by accumulations, for instance reels, of nonwoven webs T1 and T2, that in this example have equal dimensions and composition. In this example, the nonwoven webs have bicomponent fibers of the coaxial type. For example, the inner part of the inner coaxial fibers is made of polyethylene, whilst the outer part is made of polypropylene. These nonwovens are preferably spun bound.

The plant 10 furthermore comprises a calender 14 for joining, through spot welding, the web of film F produced by the extruder 11 with two nonwoven webs T1 and T2 coming from the reels 12 and 13. It should be noted that at least part of the materials forming the outer layers of the elastic film are thermally compatible with at least part of the materials forming the fibers of the nonwoven web they respectively face.

At least one nonwoven web (and preferably both the webs) has a thickness, before entering the calender, comprised between 0.1 mm and 0.6 mm, and more preferably between 0.15 mm and 0.5 mm. In this example, the thickness is equal to 0.199 mm. Each nonwoven web has a weight, before entering the calender, comprised between 10 g/m² and 40 g/m², and in this example the weight is approximately 20.37 g/m².

The elastic film F has a thickness, before entering the calender 14, comprised for example between 0.04 mm and 0.14 mm, and in this example it is approximately 0.05 mm. The thickness of the inner layer F2 of the film F is comprised between 0.017 mm and 0.075 mm, and in this example it is approximately 0.045 mm. The ratio between the sum of the thicknesses of the two outer layers and the thickness of the inner layer of the coextruded elastic film entering the calender is comprised between 113 and 1/25 and more preferably between 117 and 1/21. In this example the ratio is 1/9.

The laminate is produced in line. Practically, the production line implemented with the plant 10 has three branches L1, L2, L3, that are respectively for the film web and the two nonwoven webs and join in the calender 14, and a fourth branch L4, exiting from the calender, where the webs F, T1 and T2 are joined together.

According to preferred embodiments, at least part of the materials forming the outer layers of the elastic film are thermally compatible with at least part of the materials forming the fibers of the nonwoven web they respectively face.

Thermal compatibility means the ability of two materials to remain joined together after heat-welding, or to remain joined together when they are thermally fused above each other and then cooled.

Along the line branch L4, downstream of the calender 14, a cooling station 15 is provided for the semi-finished laminated product P1 (formed by the three webs T1, F and T2 joined together through spot welding in the calender), for example of the type with known cooling rollers.

A cross stretching station 16 is provided downstream of the cooling station 15 for stretching the semi-finished laminated product P1 in CD. This cross stretching station 16 is, for example, of the type called “Ring Rolls.” The web exiting from the cross stretching station 16 substantially matches with the elastic laminated product P according to the invention. The elastic laminate may be cut into portions of the desired length, that are wound in reels and stored.

The elastic laminate therefore comprises the polymer intermediate elastic film F formed by the three coextruded layers F1, F2, wherein the outer layers F1 are made of the same polymer material and the inner layer F2 is made of a different polymer material, and by the two nonwovens T1 and T2 joined to the outer faces of the coextruded elastic film F through welding spots or areas Z.

The weight of the laminated product P at the end of processing is comprised between 60 and 140 g/m², and in this example it is approximately 80.2 g/m².

The thickness of the laminated product P at the end of processing is comprised between 0.5 and 0.15 mm, and in this example it is approximately 0.81 mm.

The ratio between MD elongation at break at 10 N, and laminate thickness after the stretching step is lower than 8, and preferably lower than 7.5. In this example, it is approximately equal to 6.70.

The ratio in (N/50 mm)/(mm) between CD tensile strength and thickness of the laminate P after the stretching step is lower than 79, and preferably lower than 78. In this example, it is approximately equal to 77.0. The ratio (in g/m²/mm) between weight and thickness of the laminate P after the stretching step is lower than 105, and more preferably lower than 100. In this example, it is approximately equal to 99. The welding spot or welding area density is comprised between 15 and 60 spots/cm².

The elastic film F is coextruded by means of the extruder 11. At the end of the coextrusion step, the elastic film has a temperature comprised between 220° C. and 270° C. In this example, it is approximately equal to 250° C.

The film F is fed from the extruder 11 to the calender 14. The temperature of the coextruded elastic film entering the calender after having passed through the cooling station R is comprised between 10° C. and 40° C., more preferably between 15° C. and 35° C., and in this example it is approximately 20° C.

It has been found that, adequately, a given ratio between film temperature immediately after extrusion and before the calender allows to obtain high performances in terms of elasticity and strength. The coextruded elastic film F has conveniently a temperature, when entering the calender, equal to, or lower than, 1/7 of the temperature the elastic film has at the end of the coextrusion step; conveniently, this temperature is preferably lower than 1/10.

In order to contribute to the cooling, the first web of coextruded elastic film F may adequately travel, from the extrusion step to the entrance into the calender, an air path whose length is comprised between 5 m and 20 m, and more preferably comprised between 8 m and 13 m; in this example, it is approximately 11 m at average ambient temperature (i.e. the temperature of the place where the production line is arranged).

Also the nonwoven webs T1 and 2 are fed to the calender 11 together with the film F. The calender 11 has a flat roller 14A and a roller 14B provided with appendices or protuberances, whose vertexes form the welding spots or areas Z. The temperature of the rollers 14A and 14B of the calender is comprised between 120° C. and 160° C., and in this example it is approximately 140° C. 10 Preferably, the lamination pressure between the calender rollers is comprised between 70 kg/m² and 160 kg/m².

The pressure and the temperature of the calender allows the formation of spots or areas Z where the portions of webs T1 and T1, whose dimensions are similar to those of the protuberances of the roller 14B, are fused with at least 15 corresponding portions of the outer layers F1 of the coextruded elastic film F.

In this example, after having exited the calender, the semi-finished laminated web P1 passes through the cooling station. The web P1 is cooled up to a temperature comprised between 15° C. and 40° C., in this example up to approximately 35° C.

After having passed through the cooling station 15, the semi-finished laminated web P1 passes through the mechanical stretching station 16, where it is stretched in CD. The stretching values are comprised between 150% and 250%, in this example approximately 200%.

Once the laminated web P has been stretched, it can be cut into portions of the desired length, that can be wound and stored. In order to make the laminated product P functionally transpiring or permeable, it is possible to perform a punching step, preferably between the exit of the calender 11 and the entrance of the stretching station 16, and more preferably after the cooling station, if any. The punching may be, for example, a needle punching. In other examples, the punching may be performed after the stretching step. The webs T1, T2, P1, and P move substantially continuously during the production step.

It has been found that an important aspect of the present invention is the fact of extruding the elastic film directly in the laminate production line, laminating the extruded film together with the nonwovens. Namely, a comparison has been made (see the following table) between a laminated product directly coextruded in the line, as described above (case A, with the values mentioned above), and a laminated product made by using an elastic film produced in advance, for example one month before, fed for instance from a reel, together with the nonwovens in the calender (case B).

Case A-Laminate Case B-Laminate with film with previously coextruded in line produced film MD elongation at break

at 10N (%) CD tensile strength 63.00 60.41 (

 shape) Grammage (g/m²) 80.2 79.6 Thickness (mm) 0.81 0.76 mm Softness (qualitative greater test)

 measurements according to EDANA WSP 110.4

indicates data missing or illegible when filed

Practically, it has been found that producing the coextruded elastic film in line allows a decrease of approximately 13% in the elongation at break at 10 N (value of significance for the machinability of the material on the production lines for hygienic sanitary products), an increase of about 4% in CD tensile strength (value of significance during the assembly of diapers; they break less easy), an increase of about 7% in the thickness, and a qualitatively greater softness. It is understood that what illustrated above purely represents possible non-limiting embodiments of the invention, which may vary in forms and arrangements without departing from the scope of the concept on which the invention is based. Any reference numbers in the appended claims are provided for the sole purpose of facilitating the reading thereof in the light of the description before and the accompanying drawings and do not in any way limit the scope of protection of the present invention. 

What is claimed is:
 1. An elastic laminate comprising: a polymer intermediate elastic film formed by three coextruded layers, wherein outer layers of said three coextruded layers are made of the same polymer material, and an inner layer of said three coextruded layers is made of a different polymer material from polymer material of said outer layers; two nonwoven fabrics joined, through spot or areas welding, to two opposite faces of said polymer intermediate elastic film, wherein at least one of: a ratio between MD elongation at break at 10 N, and laminate thickness after stretching of said polymer intermediate elastic film is lower than one of 8 and 7.5; a ratio in (N/50 mm)/(mm), between CD tensile strength and laminate thickness after stretching is lower than one of 79 and 78; a ratio in g/m²/mm between laminate weight and thickness after stretching is lower than one of 105 and
 100. 2. An elastic laminate according to claim 1, wherein one or more layers of said polymer intermediate elastic film are made of one or more of: elastomers comprising at least one of poly (ethylene-butene), poly (ethylene-hexene), poly (ethylene-octene), poly (ethylene-propylene), poly (styrene-butadiene-styrene), poly (styrene-isoprene-styrene), poly (styrene-ethylene-butylene-styrene), poly (ester-ether), poly (ether-amide), poly (ethylene-vinyl acetate), poly (ethylene-methyl acrylate), poly (ethylene-acrylic acid), poly (ethylene butyl acrylate), polyurethane, poly (ethylene-propylene-diene) and ethylene-propylene rubber; polymers made using polyolefins from single-site catalysts; polyolefin elastomers; and a combination of elastomers, polymers made using polyolefins from single-site catalysts and/or polyolefin elastomers.
 3. An elastic laminate according to claim 1, wherein at least part of said materials forming said outer layers of said coextruded elastic film are thermally compatible with at least part of materials of said nonwoven webs with which said outer layers are in contact.
 4. An elastic laminate according to claim 1, wherein at least one of said second nonwoven webs is extendible. 